Phase evolution, electrical properties, and conductivity mechanism in LiNbWO6
The tetragonal LiNbWO 6 (α−LiNbWO 6 ) with a trirutile structure was previously reported to have good lithium ion conductivity. However, the electrical properties of the hexagonal LiNbWO 6 (β−LiNbWO 6 hereafter) polymorph have not been reported yet mainly due to the difficulty to obtain single-phase. Herein, by quenching the sample from high temperature to room temperature at ambient air condition, a series of pure-phase β−LiNb 1- x Ta x WO 6 ( x = 0, 0.05, 0.1) materials were successfully prepared. The phase evolutions and conductivities of these materials were investigated by variable temperature X-ray diffraction and alternating current impedance spectroscopy techniques, respectively. The results revealed that lithium ion conduction also dominated in this hexagonal polymorph of LiNbWO 6 and an interesting great ionic conduction enhancement behavior was observed at a temperature region of 660–800 °C due to the minor phase transition from hexagonal to tetragonal. In addition, the possible ionic conducting mechanisms in both the tetragonal and hexagonal LiNbWO 6 materials were studied by the bond-valence-based method for the first time. The results disclosed two-dimensional and three-dimensional lithium ion migration pathways for the tetragonal and hexagonal LiNbWO 6 , respectively.
危险品化学品经营许可证（带存储）