Xingzhong Guo,Shengchi Bai,Jiaqi Shan,Wei Lei,Ronghua Ding,Yun Zhang,Hui Yang
With methylsilsesquioxane (MSQ) aerogels synthesized by the sol-gel method as a raw material and Si-Ti sol as a binder, an alcohol-based aerogel slurry consisting of only MSQ aerogel and Si-Ti sol was prepared and coated on expanded polytetrafluoroethylene (ePTFE) to form an MSQ aerogel coating layer, followed by low-temperature heat treatment. The effect of Si-Ti sol content on the microstructure of the MSQ aerogel coating layer was investigated, and the properties of a typical MSQ aerogel-layer-coated ePTFE film were evaluated. The results show that Si-Ti sol has an important role in terms of film-forming capability, surface smoothness, flexibility, and powder dropping of the MSQ aerogel coating layer. With a Si-Ti sol of 10.5 wt.% content as a binder and after heat treatment at 170 °C for 30 min, the coated ePTFE flexible thin film with a layer thickness of 30 μm shows high uniformity, integrity, and electrical insulation properties, with an elongation at break decrease over 130%, a thermal conductivity of 0.1753 W/(m·K) at 25 °C, a dielectric constant of 16.5674, and a dielectric loss of 0.06369, which can be promisingly applied in cable sheaths.
Xingzhong Guo,Jiaqi Shan,Zhongzhang Lai,Wei Lei,Ronghua Ding,Yun Zhang,Hui Yang
New flexible methylsilsesquioxane (MSQ) aerogels have been facilely prepared by a sol–gel process with methyltrimethoxysilane (MTMS) and dimethyldimethoxysilane (DMDMS) as co-precursors, followed by surface modification and ambient pressure drying. The microstructure, mechanical properties and hydrophobicity of these MSQ aerogels after surface modifications of hexamethyldisiloxane (HMDSO) and/or hexamethyldisilazane (HMDS) were investigated in detail, and the applications of surface-modified MSQ aerogels in sound-absorbance, fast dye adsorption and oil/water separation were evaluated, respectively. The MSQ aerogels surface-modified by HMDS possess flexibility, elasticity and superhydrophobicity, and demonstrate good performance in the mentioned applications. The resultant MSQ aerogel used in sound-absorbance has high frequency (about 6 kHz) acoustic absorptivity of up to 80%, benefiting from its macroporous structure and porosity of 94%, and it also possesses intermediate frequency acoustic absorptivity (about 1 kHz) up to 80% owing to its elasticity. This MSQ aerogel can selectively separate oil from oil/water mixtures with high efficiency due to its superhydrophobicity and superlipophilicity, resulting from a lot of methyl groups, density as low as 0.12 cm3·g−1and a water contact angle as high as 157°. This MSQ aerogel can be assembled to be a monolithic column applied for fast dye adsorption, and shows selective adsorption for anionic dyes and removal efficiency of methyl orange of up to 95%.Keywords:MSQ aerogel;flexibility;sol-gel;surface modification;sound-absorbing;dye adsorption;oil/water separation
危险品化学品经营许可证（带存储）