Mg 3 Sb 2 compounds were synthesized via low-temperature solid-state reaction (SSR) and ball milling (BM), respectively, followed by spark plasma sintering (SPS) process. The effects of possible sintering pressure-induced orientation in the SPS process have been investigated in terms of the microstructure and thermoelectric transport properties. The results indicate that BM technique causes more severe Mg loss than pure SSR method, leading to distinct Sb phase existing in the product after SPS consolidation process. On the contrary, a single phase of Mg 3 Sb 2 is easily obtained with the combination of SSR and SPS techniques. Besides, these BM–SPS and SSR–SPS samples exhibit the similar microstructure as well as the same electrical and thermal transport properties parallel or perpendicular to the direction of sintering pressure. The study suggests that SSR method embodies the advantages of both the composition control and the orientation elimination in Mg 3 Sb 2 compound as compared to BM method with the specific parameters in the current work. This investigation is quite favorable for this material fabrication and the future application of thermoelectric modules and devices.
This work reports the electrical and thermal transport processes in p-type Pb-doped Mg3(1+x)Sb2−yPby (0.02 ≤ x ≤ 0.08; 0 ≤ y ≤ 0.02) compounds. Low-energy electron acceptor defects Mg vacancies are easy to form, which can provide holes and make p-type transport in the Mg3Sb2 matrix. However, with an increase in excess Mg, the transport behavior changes from p type to n type as manifested synergistically by both the Hall coefficient and Seebeck coefficient. This indicates the effective role of Mg in tuning carrier type and concentration for a pristine Mg3Sb2 compound. Upon substitution of Sb by Pb, the hole concentration slightly increases, and mobility is greatly improved by 133% at room temperature. The significant increase in mobility is attributed to the weakening ionized impurity scattering, stemming from the decreasing concentration induced by Pb doping. Thus, the power factor is enhanced with a 146% improvement at room temperature. Consequently, the figure of merit ZT of the Pb-doped sample is 1.8 times larger than the pristine one at around 300 K. Moreover, the non-degenerate transport behavior revealed by electrical properties is simply analyzed regarding the effects of minority carriers on the overall Seebeck coefficient. This study proposes a new strategy of charge compensation for improving mobility and a simple way to guide the prediction about the onset of bipolar conduction for Mg3Sb2-based compounds and other potential thermoelectric materials.
危险品化学品经营许可证（带存储）