High density negative temperature coefficient (NTC) thermistor ceramics Bi 0.2-x Ce x Sr 0.5 La 0.3 TiO 3 (0 < x < 0.05) (BCSLTO) were synthesized by the Pechini method. This work is the first to characterization analysis the excellent NTC characteristics of BCSLTO ceramics at high temperatures. BCSLTO NTC thermistor ceramics have wide operating temperature is 300 °C-1000 °C, and mild sintering conditions with the conventional sintering at 1250 °C. The important electrical performance parameters of BCSLTO ceramics are as follows: the resistivities at 300 °C, 700 °C, and 1000 °C are 3.26 × 10 9 –8.99 × 10 7 Ω cm, 2.21 × 10 5 –1.05 × 10 5 Ω cm, and 1.18 × 10 3 –1.13 × 10 3 Ω cm, respectively; the thermal constant B 300/700 is 13385.9–9408.8 K; the activity energy Ea 300/700 is 1.15–0.81 eV. The resistivity and the thermal constant B can be widely control by doping Ce. In addition, the resistivity drift improves as the Ce doping content increases (below 5%). The new high-temperature Bi 0.2-x Ce x Sr 0.5 La 0.3 TiO 3 ceramic materials with mild sintering conditions, wide operating temperature and high-temperature stability can be used as potential candidates for high temperatures and harsh environments.
A series of novel high temperature negative temperature coefficient (NTC) composite ceramics based on (1- x )CaMn 0.05 Zr 0.95 O 3 - x NiMn 2 O 4 ( x = 0, 0.1, 0.2, 0.3) were fabricated by using the solid-state method. The Rietveld refinement method and backscattered electron (BSE) image confirmed the absence of any other phase. The conduction mechanism of the composite ceramics was determined by analyzing the complex impedance and resistance-temperature characteristics, which could be related to the formation of a continuous Mn 3+ -O-Mn 4+ network. The effect of spinel content on the high temperature stability was analyzed using aging tests. The ρ 400°C , ρ 700°C and B 400/700 values of the NTC thermistors were determined to be 4.9 × 10 6 –1.2 × 10 4 , 1.4 × 10 5 –0.8 × 10 3 Ω cm and 12739-5712 K, respectively. This indicated that the electrical properties could be tuned by adjusting the weight ratio of CaMn 0.05 Zr 0.95 O 3 and NiMn 2 O 4 . The findings obtained in this study reveal that the composite NTC thermistor exhibits a good application potential at high temperatures and under harsh environments.
危险品化学品经营许可证（带存储）