Controlled synthesis of lanthanide-doped Gd2O2S nanocrystals with novel excitation-dependent multicolor emissions
Developing multicolor-emitting materials has significant value in many research fields such as displays, bioimaging, and information storage. The widely adopted strategies to realize multicolor emission are tuning the material composition, phase, and size. Herein, the emission color was continuously controlled from yellow to pink by simply changing the excitation wavelength from 254 nm to 365 nm for Tb3+/Eu3+ co-doped Gd2O2S NCs. The Gd2O2S NCs with different morphologies, including nanoplate with various sizes and flower-like, were successfully prepared by seed-mediated, Na+/Y3+ co-doped, and S concentration-tuned methods. The results indicated that Na+ ions greatly promote the growth of Gd2O2S NCs and Y3+ ions have an impact on their shape. Moreover, the PL intensity of the 2%Eu-doped flower-like Na/Y:Gd2O2S (F-NYG) NCs decreased by about 24.7%, 6.8%, and 5.1% under 254 nm, 316 nm, and 348 nm excitation, respectively; this is due to less non-radiative relaxation paths above the excited state of Eu3+:5D0 at longer excitation wavelength, which result in a decreased degree of the PL intensity reduction.
危险品化学品经营许可证（带存储）