A high-energy-density NASICON-type Na3V1.25Ga0.75(PO4)3 cathode with reversible V4+/V5+ redox couple for sodium ion batteries

Yuxiang Chen,Xiangyue Liao,Peng Wang,Ji Chen,Xiaoqin Zhang,Xingqiao Wu,Sean C. Smith,Dunmin Lin,Xin Tan,Qiaoji Zheng

The stable three-dimensional framework and high operating voltage of sodium superionic conductor (NASICON)-type Na 3 V 2 (PO 4 ) 3 has the potential to work with long cycle life and high-rate performance; however, it suffers from the poor intrinsic electronic conductivity and low energy density . Herein, Ga 3+ is introduced into Na 3 V 2 (PO 4 ) 3 to activate the V 4+ /V 5+ redox couple at a high potential of 4.0 V for enhancing energy density of the materials (Na 3 V 2-x Ga x (PO 4 ) 3 ). After the partial substitution of Ga 3+ for V 3+ , three redox couples (V 2+ /V 3+ , V 3+ /V 4+ and V 4+ /V 5+ ) of V are reversibly converted in the voltage range of 1.4–4.2 V, suggesting multi-electrons (>2e − ) involved in the reversible reaction, and simultaneously the electronic conductivity of the materials is effectively enhanced. As a result, the cathode with x = 0.75 exhibits excellent electrochemical properties: in the voltage range of 2.2–4.2 V, delivering an initial capacity of 105 mAh/g at 1C with a capacity retention rate of 92.3% after 400 cycles, and providing a stable reversible capacity of 88.3 mAh/g at 40C; and in the voltage range of 1.4–4.2 V, presenting the reversible capacity 152.3 mAh/g at 1C (497.6 Wh kg −1 ), and cycling stably for 1000 cycles at 20C with a capacity decay of 0.02375% per cycle. It is found that the Na 3 V 2-x Ga x (PO 4 ) 3 cathodes possess the sodium storage mechanism of single-phase and bi-phase reactions. This investigation presents a useful strategy to enhance the energy density and cycling life of NASICON-structured polyanionic phosphates by activating high-potential V 4+ /V 5+ redox couple.