Electrochemical Behavior of Cr2+ in NaCl-CaCl2 Molten Salt and Electrodeposition of Chromium Coatings
The NaCl-CaCl2 molten salt system presents a cost-effective and stable medium for the electrodeposition of metallic chromium. However, the electrochemical behavior of Cr2+ and the deposition process for dense chromium coatings within this system remain unexplored. Using CrCl2 as a precursor, this study investigated the electrochemical behavior of Cr2+ in NaCl-CaCl2 molten salt at 620 °C through cyclic voltammetry and square wave voltammetry. The results revealed that the reduction of Cr2+ involved a one-step, two-electron exchanged reaction (Cr2++ 2e−→Cr), exhibiting quasi-reversible behavior controlled by diffusion, with a diffusion coefficient of 0.5 × 10–5 cm2s−1. Electrodeposition on a molybdenum substrate demonstrated that current density significantly influenced coating morphology. An optimal condition of 30 mA cm−2 yielded a dense and uniform chromium coating, whereas current densities of 50–70 mA cm−2 resulted in significant degradation in coating planarity due to concentration polarization. Deposition time exhibited a linear positive correlation with coating thickness. Extending deposition time eliminated initial island growth and enhanced coating continuity. X-ray diffraction confirmed the coating consisted of pure chromium phase with a strong (200) preferred orientation. This research provided a theoretical and experimental foundation for electrodepositing chromium metal coatings in the NaCl-CaCl2 molten salt system.
危险品化学品经营许可证（带存储）