Enhanced energy storage properties and antiferroelectric stability of Mn-doped NaNbO3-CaHfO3 lead-free ceramics: Regulating phase structure and tolerance factor
NaNbO 3 -based ceramics usually show ferroelectric-like P-E loops at room temperature due to the irreversible transformation of the antiferroelectric orthorhombic phase to ferroelectric orthorhombic phase, which is not conducive to energy storage applications. Our previous work found that incorporating CaHfO 3 into NaNbO 3 can stabilize its antiferroelectric phase by reducing the tolerance factor ( t ), as indicated by the appearance of characteristic double P-E loops. Furthermore, a small amount of MnO 2 addition effectively regulate the phase structure and tolerance factor of 0.94NaNbO 3 -0.06CaHfO 3 (0.94NN-0.06CH), which can further improve the stability of antiferroelectricity. The XRD and XPS results reveal that the Mn ions preferentially replace A-sites and then B-sites as increasing MnO 2 . The antiferroelectric orthorhombic phase first increases and then decreases, while the t shows the reversed trend, thus an enhanced antiferroelectricity and the energy storage density W rec of 1.69 J/cm 3 at 240 kV/cm are obtained for 0.94NN-0.06CH-0.5%MnO 2 (in mass fraction). With the increase of Mn content to 1.0 % from 0.5 %, the efficiency increases to 81 % from 45 %, although the energy storage density decreases to 1.31 J/cm 3 due to both increased tolerance factor and non-polar phase.
危险品化学品经营许可证（带存储）