The high energy density and efficiency of PVDF-based composites with double-shell Nd-BaTiO3 particles as fillers
Flexible dielectric capacitors are becoming shining stars in modern electronic devices. Ceramic particles with large dielectric constants and benign compatibility are attractive candidates to enhance the energy storage density of pristine polymer capacitors while guaranteeing their flexibility. In this work, double-shell structure of Al 2 O 3 (AO) and dopamine (PDA) were successively coated on the Nd-doped BaTiO 3 (NBT) particles and then introduced into the Poly(vinylidene fluoride) (PVDF) matrix. Obvious enhancement in dielectric constants was observed while the dielectric loss remained nearly constant. For the composite films with 1–4 vol.% NBT@AO@PDA NPs, the maximum energy density of 9.1 J/cm 3 and energy efficiency of 65% was achieved at 430 MV/m in the sample with 1 vol.% filling ratio, which are 1.4 and 1.3 times larger than those of pristine PVDF at 450 MV/m. The finite element simulation reveals the effective relief of the electric field concentration in the composite film induced by the AO and PDA layers. The greater improvement in the energy storage performance could be anticipated if the dispersity of NBT@AO@PDA NPs was further improved.
危险品化学品经营许可证（带存储）