Ti3C2Tx/Ni0.2Mn0.4Zn0.4Fe2O4 ferrite nanocomposites: Dual-loss mechanism with engineered composition for microwave absorption
Ni 0.2 Mn 0.4 Zn 0.4 Fe 2 O 4 (NMZF) nanoparticles were anchored on the surface of MXene(Ti 3 C 2 T x ) to form Ti 3 C 2 T x /NMZF nanocomposites for optimization of microwave absorption performance. The Ti 3 C 2 T x /NMZF nanocomposites were synthesized by using a four-step strategy, including sonication, stirring, hydrothermal reduction and vacuum drying. More than 40 percent of the NMZF nanoparticles in this nanocomposite were assembled to form a conductive network. Meanwhile, the multilayer MXene acted as a framework to host the NMZF nanoparticles, providing dipolar polarization, interfacial polarization and eddy current loss. Benefiting from the structure design of MXene, combined with magnetic materials and optimized impedance matching, the Ti 3 C 2 T x /NMZF exhibited a minimum reflection loss (RL min ) of −57.39 dB, with a thickness of 2.97 mm and an effective absorption bandwidth (EAB) of 3.2 GHz. Therefore, such a facile method could be used to construct nanocomposites with microwave absorption performance (-57.39 dB, 3.2 GHz), so as to address microwave pollution issues.
危险品化学品经营许可证（带存储）