Electrodeposition of NiW/ZrO2 nanocrystalline film reinforced by CeO2 nanoparticles: Structure, surface properties and corrosion resistance
To enhance the performance of nickel-tungsten (Ni W) matrix, Ni W/ZrO 2 CeO 2 nanocrystalline films have been fabricated by electrodeposition in the presence of zirconia (ZrO 2 ) and ceria (CeO 2 ) nanoparticles . The influences of process parameters on microstructural, surface properties and corrosion resistance of the nanocrystalline films were examined. Studies indicated that the fabricated films are dense, homogeneous and without cracks, comprising 23.7–28.7 wt% W, 3.9–4.9 wt% ZrO 2 and 0.45–0.68 wt% CeO 2 . The film prepared at average current density ( I av ) of 6 A dm −2 , duty cycle ( r ) of 70% contains the highest content of ZrO 2 , CeO 2 nanoparticles with the finer structure. The average roughness ( R a ) is 79.1 nm for film formed at 2 A dm −2 . The growth rate of the film is about 0.48–0.53 μm/min at I av = 4 A dm −2 and r = 50%. The hardness first increases and then decreases with the maximum value at r = 70%, I av = 6 A dm −2 and deposition time ( t ) of 40 min, respectively. Energy disperse spectroscopy (EDS) mapping, transmission electron microscope (TEM) and cross-sectional images illustrated that the ZrO 2 and CeO 2 particles had been homogeneously incorporated in the film. The electrochemical measurements illustrate that the optimal corrosion resistance of Ni W/ZrO 2 CeO 2 film could be obtained at r = 70%, I av = 6 A dm −2 and t = 40 min. The incorporation of ZrO 2 CeO 2 in Ni W film would enhance the anti-corrosion properties and hardness. Ni W/ZrO 2 CeO 2 film owns superior hardness and excellent anti-corrosion properties, showing a broad application prospect in harsh environment.
危险品化学品经营许可证（带存储）