Constructing NiFe-LDH@NixCoySe2/NF nanosheets heterojunction for high-current-density efficient water oxidation
Low-cost and high-efficiency electrocatalysts produced by constructing the interfacial heterostructure have attracted more attention in oxygen evolution reaction (OER). Herein, we synthesize a three-dimensional (3D) heterogeneous structure of Ni x Co y Se 2 nanospheres loaded onto NiFe hydroxide (NiFe-LDH) nanosheets via bare nickel foam (NF) two-step electrodeposition. The optimal NiFe-LDH@Ni x Co y Se 2 /NF nanosheets heterojunction electrocatalyst is verified with an excellent OER performance in 1.0 M KOH solution, which only requires a low overpotential of 265.5 mV and 297.8 mV to drive high current density of 100 mA cm −2 and 500 mA cm −2 , respectively, long-term durability of more than 60 h at 100 mA cm −2 , and an extremely low Tafel slope of 57.5 mV dec −1 . Meanwhile, due to the dramatic improvement in OER performance, there is an enhancement in the overall water-splitting activity of the NiFe-LDH@Ni x Co y Se 2 /NF nanosheets heterojunction, attaining a current density of 20 mA cm −2 at the low cell voltage of 1.65 V. As a result, it shows the importance of constructing highly efficient OER catalyst with the rational design of heterostructures. The enhanced catalytic performance can be attributed to the large exposed electrocatalytic active sites accessible and constructed an efficient electronic transmission channel by eliminating contact resistance.
危险品化学品经营许可证（带存储）