The nanocomposite materials of poly(3,4-ethylenedioxythiophene)/graphene oxide (PEDOT/GO), poly(3,4-ethylenedioxythiophene)/MnO 2 (PEDOT/MnO 2 ), and poly(3, 4-ethylenedioxythiophene)/graphene oxide/MnO 2 (PEDOT/GO/MnO 2 ) were successfully prepared by facile and template-free solution method. The structure and morphology of nanonanocomposites were characterized by Fourier transform infrared spectroscopy (FTIR), ultraviolet–visible absorption spectra (UV–vis), field emission scanning electron microscope (FESEM), X-ray diffraction (XRD), and energy-dispersive X-ray spectroscopy (EDX), respectively. The catalytic activities of nanocomposites were investigated through the degradation processes of methylene blue (MB) solution under dark, UV light, and nature sunlight irradiation, respectively. The results displayed that nanocomposites were successfully synthesized, and PEDOT/GO had higher conjugation length and doped degree than pure PEDOT. However, the introduction of MnO 2 could lead to the reduction of conjugation length and doped degree in PEDOT/MnO 2 and PEDOT/GO/MnO 2 nanocomposites. The field emission scanning electron microscope (FESEM) analysis also showed that both MnO 2 and GO had some effect on the morphology of nanocomposites. The catalytic activities of pure PEDOT and nanocomposites were in the order of PEDOT/GO/MnO 2 > PEDOT/MnO 2 > PEDOT/GO > pure PEDOT. Besides, the catalytic results also showed that the highest degradation efficiency of MB after 7 h occurred in the PEDOT/GO/MnO 2 composite in three irradiation.
A facile and low-cost method is presented to synthesize graphite/PEDOT/MnO2 composites with controlled network structures on commercial supercapacitor separator (CSS) membranes for high-performance supercapacitors, in which pencil lead and a cellulose-based commercial supercapacitor separator membrane were applied as the graphite source and the flexible substrate, respectively. The dependence of PEDOT and MnO2 loading on the structural formation, the electrochemical performance of the hybrid electrode, and the formation mechanism of MnO2 nanowires are systematically investigated. The optimized electrode possesses a high areal capacitance of 316.4 mF/cm2 at a scan rate of 10 mV/s and specific capacitance of 195.7 F/g at 0.5 A/g. The asymmetric supercapacitor device assembled using optimized CSS/Graphite/PEDOT/MnO2 electrode and activated carbon electrode exhibits a high energy density of 31.4 Wh/kg at a power density of 90 W/kg and maintains 1 Wh/kg at 4500 W/kg. After 2000 cycles, the device retains 81.1% of initial specific capacitance, and can drive a mini DC-motor for ca. 10 s. The enhanced capability of the CSS-based graphite/PEDOT/MnO2 network electrode has high potential for low-cost, high-performance, and flexible supercapacitors.
危险品化学品经营许可证（带存储）