Biomimetic mineralization of nacre-inspired multiple crosslinked PVA/CaAlg/SiO2 membrane with simultaneously enhanced mechanical and separation properties
Inspired by the natural nacre structure, we propose a new strategy to fabricate mineralized, multiple crosslinked hydrogel membranes with the “rigid silica in soft polymer” nacre-like structure. In-situ SiO 2 nanoparticles (NPs) and polyvinyl alcohol/sodium alginate (PVA/NaAlg) are used to simulate the rigid “bricks” and soft “mortar” compositions of nacre, respectively. The nacre-like mineralized (PVA/CaAlg/SiO 2 ) membrane showed a higher tensile strength of 4.1 ± 0.08 MPa, excellent pure water flux of 170 ± 3 L/m 2 h, and an oil/water rejection rate of 99 %. The interwoven hierarchal structure, similar to nacre, was determined by SEM analysis . In addition, incorporating SiO 2 NPs increases the anti-swelling, roughness, and hydrophilicity of the membranes. PVA/CaAlg/SiO 2 membrane exhibited excellent superhydrophilicity (WCA value was 0°) and superoleophobicity underwater (OCA value was 162°). PVA/CaAlg/SiO 2 membrane also showed excellent separation performance for water-soluble organic pollutants and can be used for dye separation with rejection efficiencies of 99.5 %, 99.1 %, and 98.3 % for Congo red (CR), Alizarin red (AR), and Sunset yellow (SY), respectively. Moreover, PVA/CaAlg/SiO 2 membrane had outstanding long-term filtration and antifouling performance. The biomineralization-inspired structure provides a promising technique that can be used to prepare high-performance organic-inorganic membranes with great promise for wastewater separation application.
危险品化学品经营许可证（带存储）