The majority of previously reported cathodic electrochemiluminescence (ECL) systems often required very negative potential to be carried out, which has greatly limited their applications in the sensing field. Screening high-performance cathodic ECL systems with low triggering potential is a promising way to broaden their applications. In this work, rhenium disulfide nanosheets (ReS 2 NS) have been revealed as an efficient co-promoter to realize low-triggering-potential cathodic luminol ECL. One strong cathodic ECL signal appeared at a potential of −0.3 V and one anodic ECL peak was obtained at −0.15 V under the reverse potential scan, which were caused by electrogenerated reactive oxygen species (ROS) from hydrogen peroxide. The generation of strong luminol ECL at low potential was the result of the electrocatalytic effect of ReS 2 NS on the reduction of H 2 O 2 . The scavenging effect of uric acid (UA) on the ROS could significantly inhibit the cathodic ECL. As a result, an ECL sensor was proposed, which showed outstanding performance for the detection of UA in the range of 10 nM to 0.1 mM with a low detection limit of 1.53 nM. Moreover, the ECL sensor was successfully applied in the sensitive detection of UA in real samples. This work provides a new avenue to establish a low-potential cathodic ECL system, which will sufficiently expand the potential application of cathodic ECL in the sensing field.
Jun Xu,Fang Cao,Xiaoyuan Yang,Xing Chen,Yan Zhang,Junwei Chen,Liqing He,Wenpei Kang
In this work, the nanocables of few-layered ReS 2 nanosheets sandwiched between carbon nanotubes (CNTs) and nitrogen-doped amorphous carbon (NC) coating (i.e., CNT@ReS 2 @NC) are synthesized as high-performance anodes of both potassium-ion batteries (PIBs) and sodium-ion batteries (SIBs). The CNT@ReS 2 @NC nanocables with dual carbon modifications have the several advantages for efficient K + /Na + storage. The few-layered ReS 2 nanosheets with a wide interlayer spacing of 0.64 nm contribute to accelerated reaction kinetics for fast K + /Na + intercalation/extraction. The carbon nanotube skeleton with a hollow interior can effectively relieve the volume change and serve as a robust conductive network to boost structural stability . The NC layer provides rich defects as active sites and suppresses the shuttle effect of polysulfides produced in discharge/charge processes. Consequently, the CNT@ReS 2 @NC nanocables possess outstanding electrochemical performance in both PIBs and SIBs owing to the synergistic effect from the different components. A long cycling lifespan of 3500 cycles with a maintained discharge capacity of 125 mAh/g is achieved for CNT@ReS 2 @NC at 1 A/g in PIBs. In SIBs, it can keep a high capacity of 202 mAh/g over 3000 cycles at 5 A/g. Moreover, the CNT@ReS 2 @NC||Na 3 V 2 (PO 4 ) 3 full cell can exhibit remarkable cycling performance, yielding a low capacity decay rate of 0.019 % per cycle over 1000 cycles at 2C.
危险品化学品经营许可证（带存储）