Xiaohui Yang,Guangping Wan,Shujuan Ma,Hongjun Xia,Jun Wang,Jiawei Liu,Yanna Liu,Gang Chen,Quan Bai
Recently, superficially porous particles (SPPs) have been intensively studied and employed for highly efficient and fast separations. In this paper, the SiO 2 @SiO 2 SPPs were synthesized by an improved polymerization-induced colloid aggregation (PICA) method using urea-formaldehyde polymer as the template. The agglomeration of silica core during modification with ureidopropyltrimethoxysilane (UPS) can not only be avoided by reflux in neutral ethanol solution, but also the secondary nucleation of the colloidal silica sol can be inhibited via optimizing the reaction conditions including pH, temperature, colloidal silica sol concentration and the reaction time. The shell thickness and pore size of SPPs can be controlled successfully by adjusting the weight ratio of silica core/colloidal silica sol and the particle size of colloidal silica sol, respectively. The SPP-C18 columns packed using octadecyltrichlorosilane (ODS) modified SPPs with different pore sizes were employed to separate small solutes and proteins. The baseline separations of 6 kinds of alkyl benzenes and 5 kinds of aromatic alcohol homologues were achieved within 4 min by the SPP-C18 column with 8 nm pore size. Compared with the commercial BEH-C18 column, more than 50,000/m of the plate number of propylbenzene was obtained, and the former provided higher column efficiency to separate small solutes than the latter. Meanwhile, 6 kinds of proteins were also separated completely within 2 min using the SPP-C18 column with 40 nm pore size. In addition, the SPP-C18 capillary column was applied to separate and identify the BSA/HeLa/mouse liver digests with capillary LC-MSMS, respectively. The results indicate that more proteins and peptides can be identified using SPP-C18 capillary column compared with commercial silica-C18 capillary column. The result demonstrates that the prepared SPP-C18 column provides higher column efficiency and the SPPs synthesized with the improved PICA method shows a great potential application for the fast separation of small solutes and proteins.
Changwei Tang,Zilong Yang,Changle Li,Jiawei Liu,Quan Bai
The polymerization-induced colloid aggregation (PICA) method is commonly used to create SiO 2 @SiO 2 core–shell silica microspheres (CSSMs), but it often encounters challenges such as incomplete shell coating and poor reproducibility. In this paper, the formation mechanism of the silica shell layer during the preparation of SiO 2 @SiO 2 CSSMs using the PICA method was investigated. It was found that ureido modification can reduce the Zeta potential of the silica core surface, facilitating the deposition of coacervates formed by urea-formaldehyde resin (UF) and silica nanoparticles on the silica core surface to form the SiO 2 shell layer when the Zeta potential of the surface is in the range of −20.1 mV to −4.8 mV. By controlling the interfacial state and surface potential of the SiO 2 core, the issue of inconsistent reproducibility in preparing SiO 2 @SiO 2 CSSMs can be overcome. Furthermore, optimization of experimental parameters such as pH, reaction temperature, water content, and reaction time can enhance the formation process. The thickness of the shell and pore size of CSSMs can be successfully adjusted by varying the reaction time and the particle size of colloidal silica sol, respectively. With optimal conditions, the semi-scale production yield of SiO 2 @SiO 2 CSSMs can be increased to 50 g. The SiO 2 @SiO 2 CSSMs were modified with octadecyltrichlorosilane (ODS) to be used as stationary phases in reversed phase liquid chromatography (RPLC) for fast separation of small solutes, peptides, and proteins. The superior separation efficiency indicates that the improved PICA method has the potential to be utilized as an alternative to the layer-by-layer method for large-scale production of SiO 2 @SiO 2 CSSMs.
危险品化学品经营许可证（带存储）