A coral-like hematite photoanode on a macroporous SnO2: Sb substrate for enhanced photoelectrochemical water oxidation
Oxygen evolution over semiconductor photoanodes plays a decisive role in water splitting via photoelectrochemical (PEC) process. While the hematite photoanode with a photocurrent threshold of 600 nm is promising for practical PEC water oxidation, it still suffers from the small minority carrier diffusion length, which makes it difficult to realize adequate light absorption and efficient charge separation concurrently. To address this issue, hematite nanorods were grown on macroporous SnO 2 :Sb substrates, forming a coral-like hematite (ATO-Fe 2 O 3 ) photoanode. The ATO-Fe 2 O 3 photoanode exhibited a 150 mV cathodic shift of onset relative to Fe 2 O 3 nanorods directly on planar SnO 2 :F (FTO-Fe 2 O 3 ). The photocurrent density reached 1.32 mA cm −2 at 1.23 V vs. RHE, approximately 8.8 times higher than FTO-Fe 2 O 3 , and it was further increased to 1.81 mA cm −2 after passivation with a thin TiO 2 overlayer. The improved photocurrent was attributed to the increased light harvesting, reduced charge transfer resistance (R ct ), and smaller contact area of oxygen bubble to hematite photoanode. Our research confirmed the effectiveness of macroporous ATO templated coral-like morphology on balancing the adequate light absorption and efficient charge separation issues of hematite photoanodes. This research may also be applicable to other semiconductor photoanodes for high-efficiency PEC water splitting.
危险品化学品经营许可证（带存储）