Construction of SnO2 buffer layer and analysis of its interface modification for Li and Li1.5Al0.5Ge1.5(PO4)3 in solid-state batteries
SnO 2 layer between Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 (LAGP) and lithium anode was prepared through simple scratch-coating process to improve interface properties. The physical phase, morphology, and electrochemical properties of Li/SnO 2 /LAGP structure were characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and electrochemical analytical methods. It was found that SnO 2 layer effectively improved the interface stability of LAGP and lithium anode. The prepared Li/SnO 2 /LAGP/SnO 2 /Li symmetric cell exhibited a large critical current density of 1.8 mA cm −2 and demonstrated excellent cycling characteristics. The polarization voltages of symmetric cell were 0.1 V and 0.8 V after 1000 h of cycling at current densities of 0.04 mA cm −2 and 0.5 mA cm −2 , respectively. Li/SnO 2 @LAGP/LiFePO 4 solid-state full cells were also assembled, exhibiting a discharge specific capacity of 150 mAh g −1 after 200 cycles at 0.1C with capacity retention rate of 96 %. The good interface properties of Li/SnO 2 /LAGP structure are attributed to the transformation of SnO 2 layer into a buffer layer containing Li 2 O, Sn 0 , and Li x Sn y alloy during cycling process, which effectively inhibits the reduction reaction between LAGP and lithium anode.
危险品化学品经营许可证（带存储）