Effect of annealing temperature in carbon powder on thermoelectric properties of the SrTiO3−δ single crystal in the [111] crystal orientation
SrTiO 3 is a promising thermoelectric material for applications in harsh environments, owing to its excellent thermoelectric (TE) properties and high-temperature stability. The effect of annealing in carbon powders on the TE properties of SrTiO 3−δ in the [111] direction was experimentally investigated and analysed using first-principles calculation. The electrical conductivity of the SrTiO 3−δ single crystals in the [111] direction increases with an increase in annealing temperature in the range of 1573–1673 K, which is opposite to that in the [510] direction as shown in a previous experiment. This is attributed to the different variation trend of carrier concentration. First-principle calculation results show that the carrier concentration in the [111] direction increases with increasing oxygen vacancy concentration, but it is the opposite in the [510] direction. Strong anisotropy of carrier concentration should be caused by the difference in atomic arrangement, making difference in the amount of free electrons that maybe constrained at high oxygen vacancy in different directions. Although the SrTiO 3−δ single crystal annealed at 1573 K shows a lower electrical conductivity, it obtains higher power factor with the maximum value of 2.24 mW m −1 K −2 at 323 K, which is predominantly due to its higher effective mass. It also yields the highest ZT value of 0.18 at 873 K owing to the lower thermal conductivity . The results of this study are imperative for the design and development of perovskite TE materials.
危险品化学品经营许可证（带存储）