Ca-Poisoning Effect on V2O5-WO3/TiO2 and V2O5-WO3-CeO2/TiO2 Catalysts with Different Vanadium Loading
Ca poisoning behavior is inevitable for high-calcium content flue gas, so V2O5-WO3/TiO2(VWT) and V2O5-WO3-CeO2/TiO2(VWCeT) catalysts with different vanadium content have been prepared and the Ca-doped catalysts are compared in this manuscript. The result shows Ce addition can both promote the NO conversion and the alkali resistance. Lower Ca addition for 0.1VWCeT catalyst promotes its oxidability and Ce modification is more suitable for low vanadium catalysts. The total acidity and the reducibility of catalysts decline after Ca doping, and the reducibility of the active species on catalysts has been strengthened by Ce addition. CeO2based catalysts with lower Ca loading struggle to resist sulfur poisoning, while higher Ca loading favors SO2adsorption and also physically reduces the cerium acidification process. In the presence of SO2, additional Brønsted acid sites are formed in Ca rich catalyst. The dynamic NH3adsorption has been investigated, shows that Ca doping content on catalyst is critical for SCR reaction, and the catalyst is more susceptible to SO2initially in alkali flue gas during the actual application, but the sulfur resistance may increase with the alkali-poisoning effect aggravated by Ca doping.Keywords:Ca-poisoning;SCR reaction;NO reduction;V2O5-WO3/TiO2and V2O5-WO3-CeO2/TiO2catalysts;SO2and water;NO removal efficiency
危险品化学品经营许可证（带存储）