Superconductivity in the cobalt-doped V3Si A15 intermetallic compound
The A15 structure of superconductors is a prototypical type-II superconductor that has generated considerable interest since the early history of superconducting materials. This paper discusses the superconducting properties of previously unreported V3−xCoxSi (0 ⩽ x ⩽ 0.30) alloys. It is found that the lattice parameter decreases with increasing cobalt-doped content and leads to an decreased residual resistivity ratio value of the V3−xCoxSi system. Meanwhile, the superconducting transition temperature (Tc) also decreases with increasing cobalt-doped content. Furthermore, the fitted data show that the increase of cobalt-doped content also reduces the lower/upper critical fields of the V3−xCoxSi system. Type-II superconductivity is demonstrated in all V3−xCoxSi samples. With higher Co-doped content, V3−xCoxSi (0.15 ⩽ x ⩽ 0.30) alloys may have superconducting and structural phase transitions in low-temperature regions. As the electron/atom ratio increases, the Tc variation trend of V3Si is as pronounced as in crystalline alloys and monotonically follows the trend observed for amorphous superconductors.
危险品化学品经营许可证（带存储）