Facile synthesis of monodisperse YAG:Ce3+ microspheres with high quantum yield via an epoxide-driven sol–gel route
Spherical cerium-doped yttrium aluminum garnet (YAG:Ce3+) phosphor particles can achieve both higher packing densities and lower scattering of light, and thus make it possible to obtain excellent white-light-emitting diode performance. In this study, monodisperse YAG:Ce3+ microspheres have been synthesized through a fast epoxide-driven sol–gel route and subsequent heat treatment under a reducing atmosphere. The spherical morphology was mainly influenced by the phase separation and gelation process, which could be controlled by the ratio of water/ethanol. Pluronic F127 was introduced into the sol–gel system to control the size of the YAG:Ce3+ microspheres, which significantly increased the luminescence intensity of the YAG:Ce3+ microspheres. The luminescence quantum yield of the 6 mol% Ce3+ ion doped YAG microspheres was measured to be more than 90%, which was as high as that of commercial YAG:Ce3+ phosphors. This approach may be readily applied to prepare a broad range of rare earth doped microspheres, implying a new route for the preparation of LEDs phosphors with regular shape and high quantum yield.
危险品化学品经营许可证（带存储）