APPLIED CATALYSIS B-ENVIRONMENTAL
·
2021
·
IF 19.503
Guangyao Zhai,Yuanyuan Liu,Yuyin Mao,Honggang Zhang,Lingtong Lin,Yujie Li,Zeyan Wang,Hefeng Cheng,Peng Wang,Zhaoke Zheng,Ying Dai,Baibiao Huang
CO 2 cycloaddition reaction from propylene oxide and CO 2 to cyclic carbonates is a desirable process to become carbon neutral. Photo energy can decrease the temperature and pressure needed for this reaction according to our previous results. However, the relationship between Lewis acidity and the photophysical process needs to be clarified and optimized. Hence, in this work, Zn is introduced into UiO-bpydc via the coordination of Zn with the bipyridyl group in bpydc. It is found that the introduction of Zn not only effectively activate propylene oxide, but also promote ligand to metal charge transfer (LMCT) process, which ultimately is beneficial for CO 2 activation. However, Ce plays a negative effect under light irradiation. namely, the presence of Ce facilitates the energy transfer process rather than the LMCT process.
研究领域:
材料科学
·
催化化学
·
光催化
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF HAZARDOUS MATERIALS
·
2023
·
IF 13.6
Xukai Li,Weirui Chen,Dongpo Liu,Gaozu Liao,Jing Wang,Yiming Tang,Laisheng Li
Due to its low interfacial electron migration ability and highly hydrophilic, Fe-MCM-41 (FeM) had poor activity and stability during catalytic ozonation . To this end, the secondary metal Zn and Si-F group were introduced into the framework of FeM to create surface potential difference and hydrophobic sites. Comparative characterizations showed that there existed rich acid sites with great potential difference on F-Fe-Zn-MCM-41 (FFeZnM). Additionally, because of the existence of hydrophobic and electron-withdrawing Si-F unit, the electron migration ability, hydrophobicity and acidity of FFeZnM were enhanced. The greater O 3 mass transfer was induced by Si-F group and O 3 was directly activated at Fe and Zn Lewis acid sites into •OH, •O 2 - and 1 O 2 . With •OH acting as main species, FFeZnM/O 3 achieved the superior IBP removal (93.4%, 30 min) and TOC removal (46.6%, 120 min) over those of sole O 3 and F-FeM/O 3 processes, respectively. HCO 3 - , Cl - , NO 3 - and SO 4 2- hindered IBP degradation by FFeZnM/O 3 , but high concentration humic acid (HA) exhibited promotion by forming HA-IBP complex. IBP degradation by FFeZnM/O 3 was enhanced with tap water , river water, and effluent from the secondary sedimentation tank of the sewage plant acting as medium. This study proposed an innovative approach to catalyst design for catalytic ozonation.
研究领域:
环境科学
·
材料科学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
FUEL
·
2021
·
IF 6.609
Nai-Yu Yao,Jing-Pei Cao,Jing-Ping Zhao,Zi-Meng He,Xiao-Bo Feng,Tian-Long Liu,Ze-Ying Wang,Xiao-Yan Zhao
A series of Zn-containing HZSM-5 (HZ5) with hierarchical pores (xZn(DS)) were obtained by adding different amounts of Zn(NO 3 ) 2 solution in a hydrothermal synthesis process. The performances of xZn(DS) in catalytic reforming of cellulose pyrolysis volatiles were investigated at 500 °C. The results showed that the addition of Zn during synthesis increased in the total pore volume of xZn(DS) and reduced the content of strong acid sites, and introduced new weak acid sites. The Zn species were highly dispersed inside the zeolite, and enhanced the accessibility of acid sites, so that the yields of light aromatic hydrocarbons and monocyclic aromatic hydrocarbons (MAHs) over 0.7Zn(DS) (The molar ratio of ZnO/Al 2 O 3 in the synthesis process of xZn(DS) was 0.7) were higher than those over S-HZ5 (Zn was not added in the synthesis process) and commercial HZ5. Compared with S-HZ5, the yield of MAHs over 0.7Zn(DS) increased from 92.8 to 114.1 mg/g and the coke yield decreased by 2.9%. The selectivity of MAHs over 0.7Zn(DS) was 87.7%, which was 5.3% higher than that over S-HZ5. Simultaneously, the increase in mesopores of xZn(DS) accelerated the mass transfer process, shortened the diffusion path and improved the anti-coking performance of the catalysts. In addition, this study also proposed a possible mechanism for the catalyst to adjust the distribution of aromatic products and provided a new idea for promoting the selective production of MAHs for the pyrolysis of cellulose.
研究领域:
能源化学
·
催化材料
✓ 已验证
产品关联
DOI
高影响因子
MOLECULES
·
2017
·Vol. 22
·期 2
·305
·
IF 2.861
Jingwei Rui,Fei Liu,Rijie Wang,Yanfei Lu,Xiaoxia Yang
A series of Zn-modified NaY zeolites were prepared by the liquid-phase ion-exchange method with different Zn sources, including Zn(NO3)2, Zn(Ac)2and ZnSO4. The samples were tested as adsorbents for removing an organic sulfur compound from a model gasoline fuel containing 1000 ppmw sulfur. Zn(Ac)2-Y exhibited the best performance for the desulfurization of gasoline at ambient conditions. Combined with the adsorbents’ characterization results, the higher adsorption capacity of Zn(Ac)2-Y is associated with a higher ion-exchange degree. Further, the results demonstrated that the addition of 5 wt % toluene or 1-hexene to the diluted thiophene (TP) solution in cyclohexane caused a large decrease in the removal of TP from the model gasoline fuel. This provides evidence about the competition through the π-complexation between TP and toluene for adsorption on the active sites. The acid-catalyzed alkylation by 1-hexene of TP and the generated complex mixture of bulky alkylthiophenes would adsorb on the surface active sites of the adsorbent and block the pores. The regenerated Zn(Ac)2-Y adsorbent afforded 84.42% and 66.10% of the initial adsorption capacity after the first two regeneration cycles.Keywords:Zeolite;Zinc sources;adsorption;desulfurization;ion exchange
研究领域:
化学工程
·
环境科学
✓ 已验证
产品关联
DOI
PubMed
高影响因子