Xingzhong Guo,Shengchi Bai,Jiaqi Shan,Wei Lei,Ronghua Ding,Yun Zhang,Hui Yang
With methylsilsesquioxane (MSQ) aerogels synthesized by the sol-gel method as a raw material and Si-Ti sol as a binder, an alcohol-based aerogel slurry consisting of only MSQ aerogel and Si-Ti sol was prepared and coated on expanded polytetrafluoroethylene (ePTFE) to form an MSQ aerogel coating layer, followed by low-temperature heat treatment. The effect of Si-Ti sol content on the microstructure of the MSQ aerogel coating layer was investigated, and the properties of a typical MSQ aerogel-layer-coated ePTFE film were evaluated. The results show that Si-Ti sol has an important role in terms of film-forming capability, surface smoothness, flexibility, and powder dropping of the MSQ aerogel coating layer. With a Si-Ti sol of 10.5 wt.% content as a binder and after heat treatment at 170 °C for 30 min, the coated ePTFE flexible thin film with a layer thickness of 30 μm shows high uniformity, integrity, and electrical insulation properties, with an elongation at break decrease over 130%, a thermal conductivity of 0.1753 W/(m·K) at 25 °C, a dielectric constant of 16.5674, and a dielectric loss of 0.06369, which can be promisingly applied in cable sheaths.
Expanded polytetrafluoroethylene (ePTFE) prosthetic valves have been widely used in clinical applications in Asian countries. However, these valves still have limits with regard to thrombosis, neointimal hyperplasia, restenosis, and valvar vegetation. The achievement of in situ endothelialization on implant materials is a promising way to overcome those limits. Here, heparin/collagen multilayers were fabricated on ePTFE films via a layer-by-layer (LBL) self-assembly technique, and then, the endothelial cell (EC) adhesive peptide sequence Arg-Glu-Asp-Val (REDV) was immobilized on the multilayers. After modification with the heparin/collagen multilayers with or without REDV peptide, less platelet activation and aggregation were observed, the blood coagulation time was increased, and the hemolysis rate was decreased compared to that on pristine ePTFE films. The REDV-functionalized ePTFE films positively impacted early EC adhesion, later cell proliferation and cell activity. The EC barrier was confirmed to be successfully achieved on the functionalized ePTFE film surface in vitro. The successful assembly of the REDV-functionalized heparin/collagen multilayer on ePTFE films improved the blood compatibility, anticoagulant properties, and cell compatibility of the films in vitro, and thus, represents a candidate approach for applications requiring quick in situ endothelialization in vivo.
危险品化学品经营许可证（带存储）