Mohammad Nisar,Adeel Abbas,Junze Zhang,Fu Li,Zhuanghao Zheng,Guangxing Liang,Ping Fan,Yue-Xing Chen
Enhancing the thermoelectric performance of n-type polycrystalline SnSe is essential, addressing challenges posed by elevated thermal conductivity and compromised power factor inherent in its intrinsic p-type characteristics. This investigation utilized solid-state reactions and spark plasma sintering techniques for the synthesis of n-type SnSe. A significant improvement in the figure of merit (ZT) is achieved through strategic reduction in Se concentration and optimization of crystal orientation. The co-doping with Br and Ge further improves the material; Br amplifies carrier concentration, enhancing electrical conductivity, while Ge introduces effective phonon scattering centers. In the Br/Ge co-doped SnSe sample, thermal conductivity dropped to 0.38 Wm⁻¹K⁻¹, yielding a remarkable power factor of 662 µW mK − 2 at 773 K, culminating in a ZT of 1.34. This signifies a noteworthy 605% improvement over the pristine sample, underscoring the pivotal role of Ge doping in enhancing n-type material thermoelectric properties. The enhancement is attributed to Br doping introducing additional electronic states near the valence band, and Ge doping modifying the band structure, fostering resonant states near the conduction band. The Br/Ge co-doping further transforms the band structure, influencing electrical conductivity, Seebeck coefficient, and thermal conductivity, advancing the understanding and application of n-type SnSe materials for superior thermoelectric performance.
Gong Yaru,Dou Wei,Lu Bochen,Zhang Xuemei,Zhu He,Ying Pan,Zhang Qingtang,Liu Yuqi,Li Yanan,Huang Xinqi,Iqbal Muhammad Faisal,Zhang Shihua,Li Di,Zhang Yongsheng,Wu Haijun,Tang Guodong
N -type polycrystalline SnSe is considered as a highly promising candidates for thermoelectric applications due to facile processing, machinability, and scalability. However, existing efforts do not enable a peak ZT value exceeding 2.0 in n -type polycrystalline SnSe. Here, we realized a significant ZT enhancement by leveraging the synergistic effects of divacancy defect and introducing resonance level into the conduction band. The resonance level and increased density of states resulting from tungsten boost the Seebeck coefficient. The combination of the enhanced electrical conductivity (achieved by increasing carrier concentration through WCl 6 doping and Se vacancies) and large Seebeck coefficient lead to a high power factor. Microstructural analyses reveal that the co-existence of divacancy defects (Se vacancies and Sn vacancies) and endotaxial W- and Cl-rich nanoprecipitates scatter phonons effectively, resulting in ultralow lattice conductivity. Ultimately, a record-high peak ZT of 2.2 at 773 K is achieved in n -type SnSe 0.92 + 0.03WCl 6 .
危险品化学品经营许可证（带存储）