Towards high strengthening efficiency of equiaxed and platelet-shaped alumina reinforced zirconia ceramics with textured microstructure using DLP-based stereolithography

ZrO 2 –Al 2 O 3 (ATZ) ceramics are attracting high interest in biomedical applications because of their desirable mechanical performance and biocompatibility. However, strength and toughness are mutually exclusive in structural ceramics . In this paper, based on digital light processing, novel textured ATZ ceramics with obvious crystallographic orientations were fabricated by incorporating Al 2 O 3 platelets with a high aspect ratio and equiaxed particles into the ZrO 2 matrix. The optimized fracture toughness of 16.9 ± 0.8 MPa m 1/2 was achieved in the textured ATZ ceramic, which was about 67.3 % higher than non-textured ZrO 2 ceramics, without sacrificing strength. The coupling toughening effects of macrolayer structure, equiaxed and platelet-shaped Al 2 O 3 particles, and ZrO 2 particles were responsible for the enhanced mechanical performance. The macroscale toughening of 3D-printed lamellar architecture led to effective energy dissipation. Additionally, the crack deflection and crack branching induced by dual-morphology Al 2 O 3 particles, accompanied by the phase transformation of the ZrO 2 matrix, were significant microscopic toughening mechanisms.