High efficiency and stable La3Si6N11:Ce phosphor-in-glass film for high power laser lighting

As an inorganic color conversion material, phosphor-in-glass film (PiF) has received extensive attention in the sphere of laser-driven white lighting due to its excellent integrated performance. The yellow-emitting phosphor La 3 Si 6 N 11 :Ce has excellent thermal stability and wide emission band, which makes it more competitive than Y 3 Al 5 O 12 :Ce in laser-driven white lighting. Herein, we embedded La 3 Si 6 N 11 :Ce phosphor powder in a silicate glass matrix (SiO 2 –B 2 O 3 –CaO–Na 2 O) and sintered it on a sapphire substrate. In the silica-rich glass system, the network structure of silica-oxygen tetrahedral glass is more rigid and the thermal erosion of the phosphor by the silica-based glass is less, which makes the phosphor maintain better performance after low-temperature co-sintering. The quantum efficiency in the optimized LSN phosphor-in-glass film (LSN PiF) is up to 81 %, and the thermal conductivity is 10.2 Wm −1 K −1 , showing good thermal stability. Impressively, the LSN PiF produces a bright near-white light (0.3323,0.346) at a blue laser of 5.6 W, with corresponding luminous efficiency up to 195 lm/W. Moreover, LSN PiF can maintain about 80 % of the initial luminous intensity after continuous lighting for 24 h at the incident power of 3.5 W. These outstanding properties can advance the development of LSN phosphors in high power laser lighting applications.