Preparation and Tribological Behavior of Nitrogen-Doped Carbon Nanotube/Ag Nanocomposites as Lubricant Additives

In this study, nitrogen-doped carbon nanotube/Ag nanocomposites (denoted as N-C/Ag) have been synthesized in a urea solution using a hydrothermal method. The carbon nanotubes, AgNO3solution, urea and poly-dopamine (PDA) served as carbon, silver, nitrogen and carbon sources, respectively. The results show that the diameter of the carbon tubes was about 30 nm, and the Ag nanoparticles, with a diameter of ca. 10 nm, dispersed on the carbon tube surface. The Ag particle size decreased with a lower degree of crystallinity at a high temperature in the presence of urea. The friction and wear behavior of the oil acid (OA) modified N-C/Ag (OAN-C/Ag) as an additive in liquid paraffin (LP) were studied using a four-ball friction and wear tester. The results have shown that the coefficients of friction (COFs) and wear scar diameters (WSDs) of steel balls lubricated with LP-OAN-C/Ag decreased by 27.3% and 25.3%, respectively, relative to pure LP. Tribofilms containing Ag, carbon and nitride were formed on the worn steel ball surfaces. Details, the carbon, Fe2O3, azides and nitride, Ag and alloy and other compounds on the wear scars may improve tribological properties. The synergistic effect of carbon, Ag and urea plays a critical role during sliding.Keywords:N-doped carbon nanotube/Ag nanocomposites;polydopamine;hydrothermal;wear;friction