Dual−crosslinked polyionic liquid polymer electrolyte with optimal balance of ion conductivity and mechanical properties for solid−state lithium metal battery

Polyionic liquids (PILs) are considered promising candidates for next−generation solid polymer electrolytes (SPEs) because they combine the electrochemical stability of ionic liquids with the processability/flexibility of polymers. However, the practical application of PILs−based SPEs are limited by their unsatisfactory mechanical properties in parallel with their insufficient ionic conductivity . Here, a double crosslinked PIL-based SPE with an optimal balance of ionic conductivity and mechanical properties is constructed by ultraviolet (UV) initiated polymerization. Among, the ionic liquid 1−(4−vinylbenzyl)−3−butylimidazolium bis(trifluoromethanesulfonyl)imide ([VBBIM][TFSI]) as a monomer , poly(ethylene glycol) diacrylate (PEGDA) and polyhedral oligomeric sesquisiloxane (POSS) as a functional crosslinker . As expected, the synthesized PIL−based SPE (POSS-PIL-PEGDA−1, 1 wt% POSS) shows a high ionic conductivity of 1.8 × 10 −4  S cm −1 (at 30 °C), a satisfactory tensile strength of 0.64 MPa, an ultrahigh thermal degradation temperature around 320 °C and a wide electrochemical stability window about 5.0 V versus Li/Li + . As a concept proof, the POSS-PIL-PEGDA−1 SPE can effectively inhibit lithium dendrites growth, and the assembled Li||LiFePO 4 solid−state lithium metal battery achieves a high discharge capacity and a good cycling performance. This strategy is attractive for studying the trade−off between mechanical properties and ionic conductivity of crosslinked PIL−based SPEs.