Effect of the ratio of Y2O3 and MgSiN2 sintering additives on the microstructure, thermal and mechanical properties of Si3N4 ceramics

To investigate the mechanism of the influence of the sintering additive ratio on the microstructure evolution of silicon nitride (Si 3 N 4 ) ceramics, Si 3 N 4 ceramics were prepared by gas pressure sintering using different ratios of Y 2 O 3 /MgSiN 2 as additives. Varying the ratio of Y 2 O 3 /MgSiN 2 changed the composition of the liquid phase, thereby affecting the densification process and phase transformation rate of Si 3 N 4 ceramics, and ultimately changing their microstructure. The reduction in the Y 2 O 3 /MgSiN 2 ratio raised the N/O and Si/O ratios in the system, which increased the liquid phase viscosity. The Si 3 N 4 grain distribution varied from "normal to bimodal". In the case of increasing the proportion of MgSiN 2 and prolonging the sintering time, more of the glass phase evaporated, which reduced the content of the low thermal conductivity phase and increased the continuity of Si 3 N 4 /Si 3 N 4 . Therefore, Si 3 N 4 ceramics with 1 wt% Y 2 O 3 and 5 wt% MgSiN 2 exhibited excellent properties after sintering at 1900 °C for 12 h, with thermal conductivity, bending strength , and fracture toughness of 106.7 Wm −1 K −1 , 776 MPa, and 11.66 MPa m 1/2 , respectively.