Preparation and Thermal Insulation Property of BCN-TiN Composite Aerogels by In-Situ Carbothermal Reduction/Nitridation Method

Non-oxide ceramic aerogel draws increasing attention in area of thermal insulation because of its low density, high temperature resistance and good chemical/thermal stability. Here, a BCN-TiN composite aerogel was prepared by an in-situ carbothermal reduction/nitridation method, using melamine (C 3 N 6 H 6 ), boric acid (H 3 BO 3 ), chitosan ((C 6 H 11 NO 4 ) n ) and titanium dioxide (TiO 2 ) as raw materials. The aerogel prepared at 1473 K showed a porosity high up to 97.6 pct with a density of 0.05 g/cm 3 . When testing at a temperature of 673 K, the thermal conductivity value of as-obtained composite aerogel was as low as 0.135 W/(m K). Moreover, the lightweight BCN-TiN aerogel had the high-temperature stability (at least 1473 K) and good compression strength, which ensures it a potential high-temperature insulation material in inert atmosphere. Graphical Abstract