Fe/Co decorated C@CNTs derived from bimetallic metal-organic-framework for microwave absorption with wide bandwidth

It’s a hurry to introduce a lightweight and high-efficiency microwave absorption material that is easy to synthesize, since the electromagnetic interference pollution is getting increasingly serious. Carbon-based microwave absorption material based on bimetallic metal-organic frameworks (MOFs) gets high conductivity and good magnetism at the same time, and thus can be regarded as an efficient microwave absorber with lightweight. Herein, we introduce an easy method to compose bimetallic carbon-based microwave absorbers based on ZIF-67. By changing the proportion of Fe 3+ and Co 2+ , not only the magnetism of the material can be adjusted, the amount of carbon nanotubes (CNTs) and so as the dielectric property of the material can also be regulated. The method of introducing precursors at room temperature and then calcinating at an Ar atmosphere is simple to repeat and appropriate for mass production. When the dosage molar ratio of Co 2+ : Fe 3+ is 3: 2, the minimum reflection loss ( RL min ) can reach − 24.83 dB while the effective absorption bandwidth (EAB) can reach 5.14 GHz when the thickness is 1.7 mm, under a 30 wt% filling loading. We believe that this work can provide a reliable method to introduce carbon-based microwave absorption material based on bimetallic MOF materials.