Low temperature synthesis of novel (Cr,V)-ZrSiO4 jewel green pigments with near-infrared reflection performance

Novel (Cr,V)-ZrSiO 4 jewel green pigments with near-infrared reflection performance were prepared at a low temperature of 900   °C. Effects of Cr/Si mole ratio on phase composition, microstructure, Vis–NIR reflection performance, optical properties and thermal stability were studied. The results show that with the increase of Cr/Si mole ratio from 0 to 0.4, the color of the pigment changes from blue to jewel green and then to dark green. When the Cr/Si mole ratio is 0.2, the (Cr,V)-ZrSiO 4 jewel green pigment shows the best comprehensive properties, which has rendering performance ( L *   =   56.69, a *   =   −18.52, b *   =   −9.28), thermal stability, and near-infrared reflection performance. The properties especially excellent near-infrared reflection performance make it promising functional pigment in heat insulation. Resumen Se prepararon nuevos pigmentos verde joya (Cr,V)-ZrSiO4 con rendimiento por reflejo en el infrarrojo cercano a una temperatura baja de 900 ̊C. Se estudiaron los efectos de la relación molar Cr/Si sobre la composición de fase, la microestructura, el rendimiento de reflexión Vis-NIR, las propiedades ópticas y la estabilidad térmica. Los resultados muestran que con el aumento de la relación molar Cr/Si de 0 a 0,4, el color del pigmento cambia de azul a verde joya y luego a verde oscuro. Cuando la relación molar Cr/Si es 0.2, el pigmento verde joya (Cr,V)-ZrSiO4 muestra las mejores propiedades integrales, que tiene rendimiento de renderizado (L*   =   56.69, a*   =   -18.52, b*   =   -9.28), estabilidad térmica y rendimiento de reflexión en el infrarrojo cercano. Las propiedades especialmente excelente rendimiento de reflexión en el infrarrojo cercano lo convierten en un pigmento funcional prometedor en el aislamiento térmico.