Artificial bi-functional layers promoting Zn2+ desolvation and homogeneous deposition for reversible zinc metal anodes

Rechargeable aqueous zinc-ion hybrid supercapacitors (ZHSs) are drawing extensive attention because of their cost-effectiveness and diminished safety hazards. Nevertheless, large-scale application of ZHSs has been hindered by the severe side reactions and rampant dendrites growth on the surface of Zn metal anodes. Herein, we propose a three-dimensional organic–inorganic composite frame material as an artificial bi-functional layer coated on the zinc foil, featuring nitrogenous functional groups with zincophilicity (abbreviated as NCFM@Zn). The nitrogen (N) site's strong adsorption capacity and synergistic effect of the sub-nanopore size promote rapid desolvation of zinc ions and reduce side reactions, while also prolonging galvanized nucleation's Sand's time and allowing for even nucleation. Moreover, the uniform distribution of N on the layer results in homogeneous zinc ions flux and supports consistent zinc plating while inhibiting dendrites generation. As a result of this unique artificial bi-functional layer, symmetric Zn cells can survive 2500 h at 2.5 mA cm −2 . High-areal-capacity zinc||activated carbon hybrid supercapacitors also demonstrate 20,000 cycles at high Coulombic efficiency, thus highlighting the utter convenience and potential of this strategy for modifying rechargeable metal hybrid supercapacitor surfaces.