Oxygen vacancy-rich C/Ti3C2/(001)TiO2 hollow microspheres and the photocatalytic degradation of organic pollutants

C/Ti 3 C 2 /(001)TiO 2 hollow microspheres were prepared by combining the template method, self-assembly and hydrothermal method . Anatase TiO 2 nanosheets with rich oxygen vacancies formed on the microspheres and exposed active (001) facets due to the spherical surface. TC was removed 92.3% by C/Ti 3 C 2 /(001)TiO 2 -HMs within 160 min, 28.4% by TiO 2 and 49.5% by (001)TiO 2 /Ti 3 C 2 under the same condition. The high removal efficiency of C/Ti 3 C 2 /(001)TiO 2 -HMs could be because the oxygen vacancies exposed on the surface of (001)TiO 2 afforded more active sites, extended the light absorption range and promoted the generation of electron-hole pairs. The composite C/Ti 3 C 2 /(001)TiO 2 structure could suppress the recombination of electron-hole pairs and prolong their lifetime. The degradation pathway of TC was discussed. The TC removal efficiency of C/Ti 3 C 2 /(001)TiO 2 -HMs was confirmed by treating the wastewater from the Slender West Lake. The production principle of oxygen vacancy could be used for preparing MXene composites with excellent catalytic properties and the C/Ti 3 C 2 /(001)TiO 2 -HMs could be a potential choice for treating wastewater.