Preparation of high electromagnetic interference shielding and humidity responsivity composite film through modified Ti3C2Tx MXene cross-linking with sodium alginate

This paper established a new kind of L-citrulline-modified MXene cross-linked sodium alginate composite film through solution blending and casting film methods. The L-citrulline-modified MXene cross-linked sodium alginate composite film exhibited high electromagnetic interference shielding efficiency of 70 dB and high tensile strength of 7.9 MPa, which were much higher than the sodium alginate film without L-citrulline-modified MXene. In addition, the L-citrulline-modified MXene cross-linked sodium alginate film appeared humidity responsibility in a water vapor environment, the weight, thickness, and current appeared to increase trend and the resistance appeared to decrease trend after it absorbed water, and these parameters recovered to their original values after drying.