Facile Synthesis of Reduced-Graphene-Oxide-Modified Ammonium Polyphosphate to Enhance the Flame Retardancy, Smoke Release Suppression, and Mechanical Properties of Epoxy Resin

A unique hybridized intumescent flame retardant named reduced-graphene-oxide-modified ammonium polyphosphate (RGO-APP) was successfully synthesized via the simple hydrothermal method and reduced process. Then, the obtained RGO-APP was applied in epoxy resin (EP) for flame retardancy reinforcement. The addition of RGO-APP results in a significant reduction in heat release and smoke production from the EP, which is attributed to EP/RGO-APP producing a more compact and intumescent char against the heat transfer and combustible decomposition, thus enhancing the fire safety of EP, as confirmed by char residue analysis. Especially, the EP containing 15 wt% RGO-APP acquires a limiting oxygen index (LOI) value of 35.8% and shows a 83.6% reduction in peak heat release rate and a 74.3% reduction in peak smoke production rate compared with those of pure EP. The tensile test exhibits that the presence of RGO-APP favors the enhancement in tensile strength and elastic modulus of EP due to the good compatibility between flame retardant and epoxy matrix, as supported by differential scanning calorimetry (DSC) and scanning electron microscope (SEM) analyses. This work provides a new strategy for the modification of APP, thus facilitating a promising application in polymeric materials.Keywords:epoxy resin;ammonium polyphosphate;graphene oxide;flame retardancy;char formation