Preparation of nano-porous poly(ether ether ketone) hollow fiber membrane and its performance for desalination in vacuum membrane distillation

Nano-porous poly(ether ether ketone) (PEEK) hollow fiber membranes were successfully fabricated from PEEK/polyetherimide (PEI) blends via thermally-induced phase separation (TIPS) followed by chemical extraction of PEI method. The gas permeation rates , morphologies and mechanical properties of membranes were systematically investigated under different spinning conditions. The content of PEEK in blends substantially determined the gas permeation rates following the order: PEEK30/PEI70 (~9000 GPU) > PEEK40/PEI60 (~5100 GPU) > PEEK50/PEI50 (~1700 GPU) > PEEK60/PEI40 (~300 GPU) > PEEK70/PEI30 (below 1.0 GPU). Faster winding rates and bigger N 2 bore fluid flow rates would result in bigger pores, higher porosity and larger gas permeation rates, while would cause lower mechanical strength. Furthermore, the silane-grafted hydrophobic PEEK hollow fiber membranes were successfully prepared via one-step reduction followed by silane modification. The performance of virgin and modified membranes was evaluated by treating saline feed containing 3.5 wt% sodium chloride in vacuum membrane distillation (VMD) process. Compared with virgin PEEK membrane, the modified membranes exhibited a more stable flux and higher salt rejection over 99.9 % for 33 h, indicating the significant improvement in the anti-wetting property caused by silane modification. The application attempt expands the research direction of PEEK membranes and promotes its further application potential in VMD process.