High-performance carboxymethyl cellulose-based composite film tailored by versatile zeolitic imidazolate framework

Robust biopolymer-based composite film with multifunctional performances significantly contributes to the packaging field. Herein, we proposed a sort of carboxymethyl cellulose (CMC) based composite film via incorporating versatile zeolitic imidazolate framework (ZIF) materials. Compared to pristine CMC film, the OTR, WVTR, and tensile strength of CMC/ZIF composite film with 1 wt ‰ Zn/Co-ZIF were improved from 64.89 cm 3 *μm/(m 2 *d*kPa), 1579.21 g/(m 2 *24h) and 16.9 MPa to 20.79 cm 3 *μm/(m 2 *d*kPa), 1209.58 g/(m 2 *24h) and 70.1 MPa, respectively. Notably, owing to the reduced band gap and intrinsic chemical and thermal stability of Zn/Co-ZIF, the fabricated Zn/Co-ZIF/CMC composite film presented well UV protection capability within the whole UV region and excellent UV-blocking durability after being exposed to UV-light at 365 nm for 12 h. In practice, the photocatalytic degradation of RhB solutions under UV light could be effectively suppressed when using Zn/Co-ZIF/CMC film as UV protection layer. Our findings proposed the potential application of these versatile ZIF materials as functional nanofiller within biopolymer substances for UV protection and transparent packaging area.