Dense 1,2,4,5-tetramethylimidazolium-functionlized anion exchange membranes based on poly(aryl ether sulfone)s with high alkaline stability for water electrolysis

Anion exchange membranes with enough alkaline stability and ionic conductivity are essential for water electrolysis . In this work, a class of anion exchange membranes (PAES-TMI-x) with dense 1,2,4,5-tetramethylimidazolium side chains based on poly(aryl ether sulfone)s are prepared by aromatic nucleophilic polycondensation , radical substitution and Menshutkin reaction . Their chemical structure and hydrophilic/hydrophobic phase morphology are characterized by hydrogen nuclear magnetic resonance ( 1 H NMR) and atomic force microscope (AFM), respectively. The water uptake, swelling ratio and ionic conductivity for PAES-TMI-x are in the range of 23.8%–48.3%, 8.3%–14.3% and 18.22–96.31 mS/cm, respectively. These AEMs exhibit high alkaline stability, and the ionic conductivity for PAES-TMI-0.25 remains 86.8% after soaking in 2 M NaOH solution at 80 °C for 480 h. The current density of 1205 mA/cm 2 is obtained for the water electrolyzer equipped with PAES-TMI-0.25 in 2 M NaOH solution at 2.0 V and 80 °C, and the electrolyzer also has good operation stability at current density of 500 mA/cm 2 . This work is expected to provide a valuable reference for the selection and design of cations in high-performance AEMs for water electrolysis.