Facile Synthesis of Highly Emissive All-Inorganic Manganese Bromide Compounds with Perovskite-Related Structures for White LEDs

Lead-free all-inorganic halide materials with different Mn2+-based crystal structures (Cs3MnBr5and CsMnBr3) were obtained using a convenient synthetic method. Cs3MnBr5had a bright green emission (522 nm), with a unique single-exponential lifetime (τavg= 236 µs) and a high photoluminescence quantum yield (82 ± 5%). A red emission was observed in the case of the CsMnBr3structure with a two-exponential fluorescence decay curve, and the lifetime was 1.418 µs (93%) and 18.328 µs (7%), respectively. By a judicious tuning of the synthetic conditions, a mixed phase of Cs3MnBr5/CsMnBr3was also produced that emitted white light, covering almost the entire visible spectrum. White-light-emitting diodes (WLEDs) with color coordinates (0.4269, 0.4955), a color temperature of (3773 K), and a color rendering index (68) were then fabricated using the as-prepared powder of mixed phases of Cs3MnBr5/CsMnBr3with a commercial UV LED chip (365 nm).Keywords:perovskite;Cs3MnBr5;manganese halide;phosphor;white LEDs