Enhancing the osteogenic differentiation of aligned electrospun poly(L-lactic acid) nanofiber scaffolds by incorporation of bioactive calcium silicate nanowires

Bone defects cause serious psychological and economic burden to patients. Artificially bone repairing materials bring hope to the treatment of bone defects. Electrospun technique has attracted great attention since it can fabricate fibers from nano- to micro- scale continuously. Scaffolds fabricated by electrospun can mimic the structure of extracellular matrix which is beneficial to cell adhesion and migration. Researches have showed that bioactive ions (such as silicon and calcium ions) can promote bone regeneration. In addition, physical cues can affect cellular behavior such as cell adhesion and differentiation. In this study, two kinds of calcium silicate – adopted poly (L-lactic acid) (CS-PLLA) electrospun scaffolds with random/aligned structures were prepared by electrospun to promote bone regeneration. The integration of CS nanowires improved the biological property of PLLA electrospun scaffolds. Furthermore, in vitro results indicated that aligned 1 wt% CS adopted PLLA (PCA1) electrospun scaffolds with better physical properties and facilitated cell adhesion, improved alkaline phosphate (ALP) activity and the expression of osteogenic genes (Osteopontin (OPN), Collagen type 1 (Col-1) and Bone morphogenetic protein-2 (BMP-2)) compared with random 1 wt% CS adopted PLLA (PCR1) electrospun scaffolds. In conclusion, the prepared PCA1 electrospun scaffolds might be a potential candidate for bone regeneration in defect areas.