Enhanced N-Type Bismuth-Telluride-Based Thermoelectric Fibers via Thermal Drawing and Bridgman Annealing

N-type bismuth telluride (Bi2Te3) based thermoelectric (TE) fibers were fabricated by thermal drawing and Bridgman annealing, and the influence of Bridgman annealing on the TE properties of n-type Bi2Te3-based TE fibers was studied. The Bridgman annealing enhanced the electrical conductivity and Seebeck coefficient because of increasing crystalline orientation and decreasing detrimental elemental enrichment. The TE performance of n-type Bi2Te3-based TE fibers was improved significantly by enhancing the power factor. Hence the power factor increased from 0.14 to 0.93 mW/mK2, and the figure-of-merit value is from 0.11 to 0.43 at ~300 K, respectively.Keywords:n-type Bi2Te3;thermoelectric fibers;thermal drawing;Bridgman annealing