Chitosan-based composites reinforced with antibacterial flexible wood membrane for rapid hemostasis

Irregular hemorrhagic traumas always threaten the health of patients due to uncontrollable bleeding and wound infections. The traditional hemostatic materials show dissatisfactory hemostatic efficiency and antibacterial activity in solving these potential bleeding dangers. Herein, we proposed a kind of composites based on flexible wood membrane (FWM) loaded with chitosan/alginate derivative for accelerating rapid hemostasis and preventing infection. FWM was removed part of hemicellulose and lignin by using NaOH/Na 2 SO 3 mixture to obtain excellent flexibility while retaining the original porous structure, followed by loading silver nanoparticles on the FWM surface to prepare AgNPs-FWM as an antibacterial bio-carrier. Then, AgNPs-FWM was coated with polyoxyethylene stearate-modified chitosan and multi-aldehyde sodium alginate to fabricate the composites of chitosan/alginate/AgNPs-FWM (CSA/AgNPs-FWM) using in-situ Schiff base reaction. Furthermore, in vitro and in vivo experiments showed that the CSA/AgNPs-FWM composites exhibited lower BCI value (2.6 ± 1.3 %), more rapid hemostasis (26 s) and lower blood loss (67.8 mg) than that of the traditional materials. The possible mechanism for the hemostasis process was not only the high blood absorption capacity, but also the synergistic interaction between hydrophobic alkane chains, amino groups, aldehydes, hydroxyl groups and blood cells. Moreover, CSA/AgNPs-FWM showed exceptional superiorities in mechanical properties and antibacterial activity, which endowed composites high potential in hemostasis application for irregular external wound.