Enhanced thermal conductivity in Si3N4 ceramics by carbonizing polydopamine coatings

To enhance the thermal conductivity of Si 3 N 4 , a polydopamine (PDA) coating was creatively introduced into ceramics sintered with different additive contents through a two-step sintering process consisting of a first treatment at 1500 °C for 8 h followed by 12 h at 1900 °C under 1 MPa nitrogen pressure. After the first-step sintering, the PDA-coated sample exhibited a higher elimination effect of the liquid phase and an increase in the N/O ratio, which allowed the additives to directly interact with the Si 3 N 4 grains, resulting in a microstructure with more and larger rod-shaped grains. After the second-step sintering, the densified samples of the PDA-coating attained slightly coarser rod-shaped grains, lower O content, higher N/O ratio and peak intensity (XRD) of the Y 2 Si 3 O 3 N 4 phase, thicker grain boundary film, and secondary phases mainly residing in multigrain junctions. Consequently, the thermal conductivity of all the PDA-coated samples typically showed a 10–12% increment in comparison to the PDA-free samples for each additive content.