Oxidation resistance at 900 °C of porous Ni-Al-Cr intermetallics synthesized via rapid thermal explosion reaction

Ni-Al-Cr intermetallic compounds are candidate at extreme environment due to their excellent oxidation resistance at high temperature, and the oxidation resistance of Ni-Al-Cr alloy system has been studied extensively. However, the research on oxidation resistance mechanism of porous Ni-Al-Cr intermetallic compounds is still not deep. In our work, porous Ni-Al-Cr intermetallic compounds were synthesized by thermal explosion, and the oxidation resistance of porous Ni-Al-Cr system was mainly investigated. The results indicate that Cr promotes the formation of highly protective continuous Al 2 O 3 layer, increasing the oxidation resistance at 900 °C of porous Ni-Al-Cr. After oxidation at 900 °C for 120 h, the minimum mass gain of Ni-Al-Cr products is only 6.96%.