A novel porous La2Zr2O7 ceramic aerogels with ultralow thermal conductivity and photocatalytic property

Porous La 2 Zr 2 O 7 ceramic aerogels (CAs) were prepared by sol-gel template method and thermal treated process. The microstructure and crystallisation behavior of the samples were systematically characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), and Raman spectroscopy. The results indicated that the as-prepared porous La 2 Zr 2 O 7 CAs had a single-phase pyrochlore structure with typical three-dimensional (3-D) porous structure. Meanwhile, the formation mechanisms of the as-prepared porous La 2 Zr 2 O 7 CAs were investigated. At the same time, the as-prepared porous La 2 Zr 2 O 7 CAs presented an ultralow room-temperature thermal conductivity of 0.07 W/(m K), high specific surface areas of 325.17 m 2 /g, and a relatively high compressive strength of 11.95 MPa. What's more, the as-prepared porous La 2 Zr 2 O 7 CAs possessed ideal photocatalytic activities due to its high crystallinity, large surface area as well as unique 3-D porous structure. Therefore, the present work is proposing some new insight to prepare rare-earth zirconates CAs with porous structures for thermal insulation and dye degradation applications.