Effect of sintering temperature on solidification and migration of non-volatile and volatile heavy metals in glass-ceramic

Using tailings as material to prepare glass-ceramic is an excellent way to achieve the resource utilization of solid waste. However, at present, researches on the solidification and migration of heavy metals are limited. Therefore, in this study, ten groups of samples were prepared by controlling sintering temperatures . The solidification, migration, and leaching behavior of non-volatile and volatile heavy metals were studied. The research showed that, with the increase of temperature, the properties of the samples were improved. Fe participated in the phase transformation and evolved into insoluble iron pyroxenes solid solution, while Pb was homogeneously distributed in the glass matrix of glass-ceramics. The leaching concentrations of Fe and Pb in the glass-ceramics were 0.055 mg/L ∼0.087 mg/L and 0.074 mg/L ∼0.140 mg/L, which were far below the threshold value. The results showed that heavy metals can be effectively solidified in glass-ceramics and have good environmental benefits.