Disproportionation enabling reversible MnO2/Mn2+ transformation in a mild aqueous Zn-MnO2 hybrid battery

The disproportionation of the Jahn-Teller (J-T) active manganese oxides (Mn 3+ ) often leads to uncontrollable Mn 2+ dissolution, which has been identified as one of the major causes of the performance degradation in conventional Zn-MnO 2 batteries. Herein, we use the “unwanted” disproportionation of the Mn 3+ cations to realize effective MnO 2 /Mn 2+ transformation, achieving high specific capacity (550 mAh g −1 ) and good cycling stability (5000 cycles without capacity decay) in a Zn-MnO 2 hybrid battery with mild aqueous electrolytes. Mechanism study shows that MnO 2 is deposited on the cathode during charging, H + /Zn 2+ insertion and disproportionation occur sequentially during discharging, leading to Mn 2+ dissolution. The generated high-valence manganese oxides via disproportionation further experience reduction-disproportionation-dissolution, which proceeds repeatedly in the expanded discharge potential to 0 V vs. Zn 2+ /Zn, resulting in the complete dissolution of the cathodic materials. Our results provide the fundamental understanding on the controversial mechanisms of Zn-MnO 2 batteries with mild aqueous electrolytes and highlight the effect of disproportionation in pushing the electrochemical performance of the promising Zn-MnO 2 hybrid batteries.