Thermally stable La-Ni-B amorphous additives for enhancing hydrogen storage performance of MgH2

In this work, we synthesized La-incorporated Ni-B amorphous composites and investigated their effects on enhancing dehydrogenation/hydrogenation properties of MgH 2 . MgH 2 with 5 wt% 2La-3Ni-B demonstrated significantly improved dehydriding kinetics. About 6.0 wt% hydrogen could be released within 5 min at 300 °C. Moreover, no decrease in deydrogenation rate was observed within ten cycles. XRD , XPS , SEM and HRTEM examinations revealed that the La incorporation into Ni-B resulted in an amorphous La-B-O structure that could keep its disorder state up to 600 °C. The crystallization and growth of Ni dispersed in the La-B-O structure was significantly retarded. Also the alloying of Mg with Ni or La was not observed. As a result, the added La-Ni-B composites showed higher structural and catalytic stability than Ni-B during hydriding/dehydriding cycling of MgH 2 at high temperatures.